ABS HI121H LG Chem

Nombre del producto: ABS – MFI22 – LG CHEM – HI121H
Categoría: Acrilonitrilo Butadieno Estireno
Información del manual del producto: LG ABS HI121H
Acrylonitrile Butadiene Styrene

LG Chem Ltd.

Technical Data

Product Description
Description
HI121H is a widely used ABS product for injection molding, designed to have impact resistance.

Key Features
Impact Resistance, General Purpose

Application
Electrical/Electronic Products, Miscellaneous Goods
General
Material Status
• Commercial: Active
Literature 1
• Technical Datasheet (English)

Availability
• Asia Pacific
• Europe
• Latin America
• North America

Features
• General Purpose
• Good Impact Resistance
• Electrical/Electronic
Applications
• General Purpose

Automotive Specifications
• GM GMP.ABS.002
• GM GMW15572P-ABS-T1
• IMDS ID 9607651
Processing Method
• Injection Molding
Multi-Point Data
• Specific Heat vs. Temperature (ISO 11403)

Physical
Nominal Value Unit
Test Method
Density / Specific Gravity 3
1.05 g/cm³
ASTM D792
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg)
22 g/10 min
ASTM D1238
Molding Shrinkage – Flow
23°C, 3.20 mm, Injection Molded
0.40 to 0.70 %
ASTM D955
Mechanical
Nominal Value Unit
Test Method
Tensile Strength 4
Yield, 23°C, 3.20 mm, Injection Molded
50.0 MPa
ASTM D638
Tensile Elongation 4
Break, 23°C, 3.20 mm, Injection Molded
> 10 %
ASTM D638
Flexural Modulus 5
23°C, 6.40 mm, Injection Molded
2550 MPa
ASTM D790
Flexural Strength 5
23°C, 6.40 mm, Injection Molded
82.0 MPa
ASTM D790
Impact
Nominal Value Unit
Test Method
Notched Izod Impact
23°C, 3.20 mm, Injection Molded
270 J/m
ASTM D256
23°C, 6.40 mm, Injection Molded
220 J/m
Hardness
Nominal Value Unit
Test Method
Rockwell Hardness
R-Scale, 23°C, Injection Molded
110
ASTM D785
Thermal
Nominal Value Unit
Test Method
Deflection Temperature Under Load 6
1.8 MPa, Unannealed, 6.40 mm, Injection Molded
85.0 °C
ASTM D648
Vicat Softening Temperature
93.0 °C
ASTM D1525 7
Search for UL Yellow Card
• LG Chem Ltd.
• LG ABS
Uses

Injection
Nominal Value Unit
Drying Temperature
70 to 80 °C

Drying Time
3.0 to 4.0 hr
Processing (Melt) Temp
200 to 250 °C

Mold Temperature
40 to 80 °C
Screw Speed
30 to 60 rpm