Policarbonato Resin TARFLON IR1900 MERCAI

Nombre del producto: Policarbonato Resin TARFLON IR1900
Categoría: Policarbonato
Información del manual del producto: Typical property table
Polycarbonate resin TARFLONTM
Formosa Idemitsu Petrochemical Corporation (FIPC)
General PC with iced-clear color and good mold release property for injection molding or extrusion.
IR grade is listed in NSF/ANSI standard 51 Food Equipment Materials.
Property
Method
Units
IR1900
ISO identification mark
–
–
>PC< Physical MFR ISO 1133 g/10min 19 Density ISO 1183 g/cm3 1.2 Water absorption (50%RH 24hr) ISO 62 % 0.23 Mechanical Tensile stress at Yield ISO 527-1,2 MPa 65 Tensile strain at break ISO 527-1,2 % 95 Flexural strength ISO 178 MPa 90 Flexural modulus ISO 178 GPa 2.3 Charpy impact strength (Notched) ISO 179-1 kJ/m2 70 Rockwell hardness ISO 2039-2 R/M scale R120/M50 Thermal Heat deflection temperature (1.8 MPa) ISO 75-1,2 oC 125 Linear thermal expansion coefficient ISO 11359-2 x 10-5/oC 6.5 Mold shrinkage ASTM D955 % 0.5 ~ 0.7 Optical Total luminous transmittance ISO 13468-1 % 85 ~ 90 Electrical Dielectric strength IEC 60243-1 kV/mm 30 Volume resistivity ASTM D257 Ω・cm > 1016
Dielectric Constant (1 MHz)
IEC 60250
–
2.85
Dielectric dissipation factor (1 MHz)
IEC 60250
–
0.0092
UL rating
Flammability
UL94
(Class)
V-2 (0.36 ~ 1.8 mm)
HB (1.9 ~ 6.0 mm)
CTI
UL746A
(PLC level)
2
RTI (Elec)
UL746B
oC
130
RTI (Imp)
UL746B
oC
125
RTI (Str)
UL746B
oC
130
UV, water exposure or immersion
UL746C
–
f2
Standard molding parameters
Pre-drying condition
–
–
120 oC, 5~8hours
Cylinder temperature
–
–
260 ~ 300 oC
(Max.320 oC)
Mold teperature
–
–
80 ~ 120 oC
UL file No. QMFZ2.E238753
The above typical data are supplied only for technical information, not guaranteed values.
This document may be revised without prior notice.