Resina Polietileno HDPE Formolene HB5202B2 Formosa

Nombre del producto: PE – HDPE – MFI0.3 – FORMOSA – FORMOLENE HB5202B2
Categoría: Polietileno
Información del manual del producto: 10/15

Formolene® HB5202B2

High Density Polyethylene (HDPE) Resin
Designed for Both Sheet Extrusion and Blow Molding Applications

Formolene® HB5202B2 is designed for applications requiring excellent stiffness, impact strength, and
excellent stress crack resistance. It may be used as a blow molding resin or sheet extrusion
thermoforming resin.

Formolene® HB5202B2 meets all requirements of the U.S. Food and Drug Administration as specified
in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.
Suggested Applications:
Containers…
Molded or formed…
Bleach and Detergents
Industrial Housings
Chemicals
Shrouds

Tanks
Nominal Physical Properties:
PROPERTY*
ASTM
TEST
METHOD

ENGLISH
Unit Value

SI
Unit Value
Density
D1505
g/cc
0.952
g/cc
0.952
Melt Index, Condition E,

190C/2.16 kg
D1238
g/10 min.
0.30
g/10 min.
0.30
Environmental Stress Crack
Resistance (ESCR)

Condition A, F50 (100% Igepal)

Condition B, F50

D1693
D1693

h
h

50
50

h
h

50
50
Tensile Yield Strength,

2” (50 mm) per min.
D638
Type IV
psi.
3900
MPa
27
Ultimate Elongation,

2” (50 mm) per min.
D638
Type IV
%
>600
%
>600
Brittleness Temperature
D746
°F
<-180 °C <-118 Flexural Modulus D790 psi. 190,000 MPa 1309 * Physical properties reported herein were determined on compression molded specimens prepared in accordance with Procedure C of ASTM D1928. The nominal properties reported herein are typical of the product but do not reflect normal testing variance and therefore should not be used for specification purposes. Published 6/01/01, Revised 1/04/16